Comparative study of mechanical properties of direct core build-up materials
Girish Kumar, Amit Shivrayan
Department of Prosthodontics, Including Crown and Bridge, and Implantology, Rajasthan Dental College and Hospital, Jaipur, Rajasthan, India
|Date of Web Publication||14-Jan-2015|
Department of Prosthodontics, Including Crown and Bridge, and Implantology, Rajasthan Dental College and Hospital, Jaipur, Rajasthan
Source of Support: None, Conflict of Interest: None
| Abstract|| |
Background and Objectives: The strength greatly influences the selection of core material because core must withstand forces due to mastication and para-function for many years. This study was conducted to evaluate certain mechanical properties of commonly used materials for direct core build-up, including visible light cured composite, polyacid modified composite, resin modified glass ionomer, high copper amalgam, and silver cermet cement. Materials and Methods: All the materials were manipulated according to the manufacturer's recommendations and standard test specimens were prepared. A universal testing machine at different cross-head speed was used to determine all the four mechanical properties. Mean compressive strength, diametral tensile strength, flexural strength, and elastic modulus with standard deviations were calculated. Multiple comparisons of the materials were also done. Results: Considerable differences in compressive strength, diametral tensile strength, and flexural strength were observed. Visible light cured composite showed relatively high compressive strength, diametral tensile strength, and flexural strength compared with the other tested materials. Amalgam showed the highest value for elastic modulus. Silver cermet showed less value for all the properties except for elastic modulus. Conclusions: Strength is one of the most important criteria for selection of a core material. Stronger materials better resist deformation and fracture provide more equitable stress distribution, greater stability, and greater probability of clinical success.
Keywords: Compressive strength, core build-up materials, diametral tensile strength, elastic modulus, flexural strength, mechanical properties
|How to cite this article:|
Kumar G, Shivrayan A. Comparative study of mechanical properties of direct core build-up materials. Contemp Clin Dent 2015;6:16-20
| Introduction|| |
A core build-up is a restoration placed in badly broken down tooth to restore the bulk of the coronal portion of the tooth to facilitate subsequent restoration by means of an indirect extra-coronal restoration. , Compressive and tensile strength of core materials is thought to be important because core usually replace a large bulk of tooth structure and must resist multidirectional forces for many years. , Cores are usually retained by pins, posts, and/or bonding system to facilitate their retention, and to restore the tooth to the extent to support a crown or bridge. 
Several dental materials have been used for core build-up procedures, some as direct and some as indirect, such as custom cast post and core.  The materials used for direct core build-up includes high copper amalgam, visible light cured resin composite, auto cured titanium containing composite, polyacid modified composite, resin-modified glass ionomer, and a silver cermet cement. Most of these materials were not specially developed for this purpose, but as a consequence of properties such as fluoride release, pleasing colors, adhesion to tooth structure, fast setting rates, choice of curing mechanism, and handling properties, they have found application as core build-up procedures. ,
Although many studies have compared fracture loads of simulated cores in various geometric configurations often on extracted teeth, the strength of core materials has rarely been compared. ,,, In view of the development of newer materials in the market, clinician often has uncertainties regarding the choice of best materials to achieve optimum results. A comparative evaluation of mechanical properties of direct core-build materials would help the clinician to select better products.
| Materials and Methods|| |
Details of all five materials are given in [Table 1]. This list includes two composite materials specifically developed as core build-up material ( Z-100 Restorative and Dyract) and one of the most commonly used material in clinical practice resin-modified GIC (Vitremer). The two other products were a silver cermet (Hi-Dense XP) and silver amalgam (Shofu).
The specimen dimensions for each property were selected according to International Standards Organization (ISO) 4049 (ISO, 1992). Compressive strength and diametral tensile strength were measured for cylindrical specimens, 3 × 6 (d.h.). Flexural strength and elastic modulus were measured for rectangular specimens, 25 × 2 × 2 (l.b.h.). Specimens were stored at 37 ± 1°C prior to testing. Ten specimens were made and tested for each group. Data were analyzed by Kruskal-Wallis test and Mann-Whitney U-test, with Statistical Package for Social Sciences (SPSS) version 11.5 for Windows.
Measurement of properties
All tests were carried out on an instron universal testing machine (Series IX, model 1011, UK). Compressive and flexural strength were determined at a-cross head speed of 0.5mm/min and diametral strength was carried out at 1 mm/min. Diametral tensile strength was calculated from the formula:
T = 2F/πDL,
where F is the maximum applied load (N); D is the mean diameter of the specimen (mm); and L the length (height) of specimen (mm).
Flexural strength was calculated from the following equation:
σ = 3FƖ0/2bh2
where F is the maximum load exerted on the specimen; Ɩ is the distance (mm) between the supports ±0.01 mm; b is the width (mm) of specimen immediately prior to testing; and h is the height (mm) of specimen measured immediately prior to testing.
The experimental variables of specimen size, shape, testing configuration, fabrication procedure, temperature, humidity, storage time, storage temperature, strain rate, and set time was all standardized in this study. All specimens were treated identically throughout this study, which was based on American Dental Association (ADA) Specification No. 27. Thus, comparisons among materials were appropriately made. In this study, core materials were compared at a single short setting time, but various types of material differ in their setting mechanisms. Some materials, such as glass ionomers, continue to mature for extended periods. Thus, the comparison was valid only for the 24-h setting time. However, cores may have to resist loads soon after placement, the effects of increased curing over time are small in comparison to the large differences among materials, and established specifications recommend 24-h test times.
| Results|| |
Statistical analysis for the strength of core materials was performed, and the mean valve with its standard deviation was calculated for each material. The Kruskal-Wallis test (H) and Mann-Whitney U-test (Z), with Statistical Package for Social Sciences (SPSS) version 11.5 for Windows was used. Here, the Kruskal-Wallis test (H) was used to compare the four properties for each material. The Mann-Whitney U-test was used for multiple comparisons of four properties among five different materials and the significance was found at 5% confidence level.
Compressive strength, elastic modulus, diametral tensile strength, flexural strength data, and results of the statistical analysis data are given in [Table 2] [Table 3] [Table 4] [Table 5].
Compressive strength, diametral tensile strength, flexural strength, and elastic modulus varied among different core build-up materials. Visible light cured composite (Z-100) had relatively high compressive strength, diametral tensile strength, and flexural strength compared to the other tested materials.
The compomer (Dyract) and resin-modified glass ionomer (Vitremer) showed good mechanical properties except in terms of elastic modulus.
Amalgam (Hi-Aristaloy) showed highest elastic modulus value compared to the other materials tested. Cermet glass ionomer (Hi-Dense) showed less value for all the mechanical properties except in terms of elastic modulus [Table 6].
|Table 6: Multiple comparison of compressive strength, diametral strength, fl exural strength, and elastic modulus|
Click here to view
| Discussion|| |
Considerable differences in compressive and diametral tensile strengths were discerned among core materials. The strongest material was 2 times stronger than the weakest material in compression, and 3 times stronger in dimetral tension and 4 times stronger in flexural strength [Figure 1]. Such large difference might reasonably be expected to have clinical significance. Minimum strength needed for core materials are unknown, but many of materials tested did not meet the dimetral tensile strengths required by the ADA specifications for direct filling resins (24 and 34 MPa for type I and type II materials, respectively.  Compressive strength is considered to be a critical indicator of success because a high compressive strength is necessary to resist masticatory and parafunctional forces. , Tensile strength is important because dental restorations are exposed to tensile stresses from oblique or transverse loading of their complex geometric forms. Diametral tensile testing is a common method for measuring tensile strength of brittle materials because it avoids some of the difficulties inherent in direct and flexural tensile testing. ,
|Figure 1: Comparative evaluation of compressive strength, fl exural strength, and diametral strength among various core build-up materials|
Click here to view
Amalgam has been considered to be the material of choice for cores. Both mechanical tests and Finite element analyses have indicated that amalgam cores have superior performances in comparison to resin composite cores. ,, In fatigue testing, amalgam cores have deformed less, produced smaller marginal gaps and applied lesser stresses to tooth structure than resin composite cores. ,, Amalgam cores are certainly to be preferred to glass ionomer, resin-modified glass ionomer, or glass ionomer cermet cores. ,, The dark color of amalgam may not be esthetic, but it is easy to differentiate from tooth structure during tooth preparation.  Unfortunately, the relatively slow set of amalgam delays rotary preparation of amalgam cores and has limited its use. However, developments and advances in nong2 amalgams and the new concepts of bonding dental amalgam to tooth structures have helped to ensure that amalgam remains one of the materials widely used for core build-up procedures in posterior teeth. ,
Glass-ionomer based materials were markedly weaker than the resin composite and amalgam materials [Table 2] and [Table 3]. Although some mechanical properties of resin-modified glass-ionomer materials only deteriorate slowly over time, the dimensional stability of resin-modified materials can be poor. ,, Sliver "reinforcement" did not improve the strength of Hi-dense Silver glass ionomer in comparison to conventional glass ionomer.
Although some mechanical properties of glass ionomer and resin-modified glass ionomer materials only deteriorate slowly over time, the dimensional stability of resin-modified materials can be poor. , Glass ionomers are also less fatigue-resistant than resin composites;  thus, the role of glass ionomers and glass ionomer based materials as cores must be questioned.
The results of our study indicate that, on the basis of strength alone, some resin composites may be used as alternative to amalgam cores. Resin composites have several practical advantages. They can be translucent and tooth-colored. Thus, they do not darken teeth.
They can also be selected for color contrast against tooth structure, to facilitate tooth preparation for crowns. They can be bonded to teeth using dentinal adhesives. For the convenience, either light initiated or auto-curing materials can be selected. As they set quickly, core and tooth preparations can be completed using rotary instrumentation without delay. ,
However, resin composites also have some disadvantages. Light-cured materials may not undergo complete curing if insufficient light intensity or curing time is used, too great a thickness is applied, or if they are reaching the end of their shelf lives. Although excellent adhesion to tooth structure can be achieved with dentinal bonding agents, the long-term stability of such bonds is unknown. ,,, Resinous materials may be less physically and dimensionally stable than amalgam. Sorption of water, after impression making and before casting cementation, can compromise seating. , One crown retention study showed that crowns cemented to resin composite cores were more retentive than crowns cemented to similar amalgam cores.  That result could be attributed to slight swelling of the composite resulting in tighter fitting castings. Alternatively differences in core surface roughness might account for that finding.
| Conclusions|| |
Strength is not only one criterion for selection of core material, but it is crucial. Stronger core materials better resist deformation and fracture, provide more equitable stress distributions, reduced probability of tensile or compressive failure, greater stability, and greater probability of clinical success. If other parameters are considered to be equal, the strongest core material is indicated. Although the perfect core material does not yet exist, the results of our study and other prior studies indicate that both amalgam and resin composites may be indicated for use as core materials in specific clinical situations.
| References|| |
Combe EC, Shaglouf AM, Watts DC, Wilson NH. Mechanical properties of direct core build-up materials. Dent Mater 1999;15:158-65.
Saygili G, Mahmali SM. Comparative study of the physical properties of core materials. Int J Periodontics Restorative Dent 2002;22:355-63.
Nicholls JI. Crown retention. I. Stress analysis of symmetric restorations. J Prosthet Dent 1974;31:179-84.
Yettram AL, Wright KW, Pickard HM. Finite element stress analysis of the crowns of normal and restored teeth. J Dent Res 1976;55:1004-11.
Huysmans MC, van der Varst PG. Mechanical longevity estimation model for post-and-core restorations. Dent Mater 1995;11:252-7.
Cattani-Lorente MA, Dupis V, Moya F, Payan T, Meyer TM. Comparative study of the physical properties of a polyacid-modified composite resin and a resin-modified glass ionomer cement. Dent Mater 1999;15:21-32.
Kerby RE, Knobloch L, Thakur A. Strength properties of visible-light-cured resin-modified glass-ionomer cements. Oper Dent 1997;22:79-83.
Arcoria CJ, DeWald JP, Moody CR, Ferracane JL. A comparative study of the bond strengths of amalgam and alloy-glass ionomer cores. J Oral Rehabil 1989;16:301-7.
American Dental Association Certification programs of the Council on Dental Materials, Instruments and Equipment. American National Standards Institution/American Dental Association Specification 27 for direct filling resins. Chicago: American National Standards Institution/American Dental Association; 1977.
Cho GC, Kaneko LM, Donovan TE, White SN. Diametral and compressive strength of dental core materials. J Prosthet Dent 1999;82:272-6.
Miyawaki H, Taira M, Toyooka H, Wakasa K, Yamaki M. Hardness and fracture toughness of commercial core composite resins. Dent Mater J 1993;12:62-8.
Levartovsky S, Kuyinu E, Georgescu M, Goldstein GR. A comparison of the diametral tensile strength, the flexural strength, and the compressive strength of two new core materials to a silver alloy-reinforced glass-ionomer material. J Prosthet Dent 1994;72:481-5.
Huysmans MC, van der Varst PG, Schäfer R, Peters MC, Plasschaert AJ, Soltész U. Fatigue behavior of direct post-and-core-restored premolars. J Dent Res 1992;71:1145-50.
Huysmans MC, Van der Varst PG. Finite element analysis of quasistatic and fatigue failure of post and cores. J Dent 1993;21:57-64.
Kovarik RE, Breeding LC, Caughman WF. Fatigue life of three core materials under simulated chewing conditions. J Prosthet Dent 1992;68:584-90.
Miyamoto S, Takagawa T, Nozaki A, Yanaka N, Nakamura Y, Imai Y, et al.
Study on atigue toughness of dental materials 1. Compressive strength on various luting cements and composite resin cores. Nihon Hotetsu Shika Gakkai Zasshi 1989;33:966-76.
DeWald JP, Arcoria CJ, Ferracane JL. Evaluation of glass-cermet cores under cast crowns. Dent Mater 1990;6:129-32.
Netti CA, Cunningham DE, Latta GH. Tensile strengths of composite core materials containing added colorants. J Prosthet Dent 1988;59:547-52.
Varga J, Matsumura H, Masuhara E. Bonding of amalgam filling to tooth cavity with adhesive resin. Dent Mater J 1986;5:158-64.
Staninec M. Retention of amalgam restorations: Undercuts versus bonding. Quintessence Int 1989;20:347-51.
Cooley RL, Robbins JW, Barnwell S. Dimensional stability of glass ionomer used as a core material. J Prosthet Dent 1990;64:651-3.
Mitra SB, Kedrowski BL. Long-term mechanical properties of glass ionomers. Dent Mater 1994;10:78-82.
Nicholson JW, Anstice HM, McLean JW. A preliminary report on the effect of storage in water on the properties of commercial light-cured glass-ionomer cements. Br Dent J 1992;173:98-101.
Anstice HM, Nicholson JW. Studies of light-cured glass-ionomer cements. J Mater Sci Mater Med 1992;3:447-51.
Tjan AH, Dunn JR, Lee JK. Fracture resistance of amalgam and composite resin cores retained by various intradentinal retentive features. Quintessence Int 1993;24:211-7.
Tam LE, McComb D, Pulver F. Physical properties of proprietary light-cured lining materials. Oper Dent 1991;16:210-7.
Oliva RA, Lowe JA. Dimensional stability of composite used as a core material. J Prosthet Dent 1986;56:554-61.
DeWald JP, Moody CR, Ferracane JL, Cotmore JM. Crown retention: A comparative study of core type and luting agent. Dent Mater 1987;3:71-3.
[Table 1], [Table 2], [Table 3], [Table 4], [Table 5], [Table 6]
|This article has been cited by|
||Stress generation in mandibular anterior teeth restored with different types of post-and-core at various levels of ferrule
| ||Anatolii Savychuk,Marianthi Manda,Christos Galanis,Christofer Provatidis,Petros Koidis |
| ||The Journal of Prosthetic Dentistry. 2017; |
|[Pubmed] | [DOI]|
||The influence of elastic moduli of core materials on shear stress distributions at the adhesive interface in resin built-up teeth
| ||Ayaka CHIBA,Takashi HATAYAMA,Kimisuke KAINOSE,Masatoshi NAKAJIMA,David H. PASHLEY,Noriyuki WAKABAYASHI,Junji TAGAMI |
| ||Dental Materials Journal. 2017; 36(1): 95 |
|[Pubmed] | [DOI]|